Silvery Closed Cell Cross linked Polyolefin Pipe Insulation Foam
Rolls Polyethylene Thermal Insulation Foam Sheets
Electronic cross-linked polyethylene foam also named Physical
crosslinked polyethyele foam, Irradiation crosslinked polyethylene
foam.Common abbreviations IXPE foam, IXLPE foam.It is made of
low-density polyethylene (LDPE), AC foaming agent and other powders
after being melted, mixed and extruded, and then foamed at high
temperature. IXPE has finer cells, smoother surface and better
mechanical properties than XPE.
Production process: compounding-extrusion-irradiation-foaming.
Note: IXPE foam can be made anti-static (we will talk about
anti-static IXPE later), but XPE cannot (theoretically it is
possible, but our company does not currently produce).
Specifications
- Foam Type: XPE FOAM / XLPE FOAM + AL FOIL + ADHESIVE
|
| Property | Standard | Unit | Value |
| Density | - | Kg/m³ | 28.00 |
| Tensile Strength | Transverse | ISO-1798 | MPa | 0.33~0.35 |
| Longitudinal | | | 0.35~0.41 |
| Tearing Strength | Transverse | ISO-8067
| Kn/m | 1.52~1.60 |
| Longitudinal | | | 1.94~2.00 |
| Compression 25% | ISO-3386-1 | kPa | 29.60 |
| Compression 45% | ISO-3386-1 | kPa | 54.40 |
| Compression 50% | ISO-3386-1 | kPa | 79.50 |
| Compression Set 25% 0.5H | ISO-1856 | % | 16.50 |
| Compression Set 25% 24H | ISO-1856 | % | 4.90 |
| Operating Temperature Range | Internal | °C | (-40,+80) |
| Water Absorption % Volume (Maximum) | Internal | % | 0.50 |
| Thermal Conductivity | JIS A1412-2 | W/mK | 0.040 |
| Shore - C | ASTM D2240 | °C | 30 |
| Flammability | FMVSS302 | mm/min | - |
Property
- Ducts are also available in both, stainless steel and Aluminum.
- Prevents Condensation on Ducts: XPE insulation provides a solid
cover around the air ducts.
- Saves Energy: retain the temperature of the air they are
transporting, reducing energy wastage.
- Hot-dipped galvanized steel sheets of lock-forming quality are used
for the manufacturing of standard ducts.
- All straight ducts have beading all along at a distance of 300 mm
between them for reinforce.
- Reduces Noise Transmitted Indoors: XPE can carry sound waves all
around the house and carry sounds across rooms such as the noise of
the furnace turning on in phases as well.
Raw material: LDPE, PE foam+Alu foil
Density: 25~333kg/m3
Length: customized
Wide: 70~1800 mm
Thickness:
xpe 2~3mm 3~12mm
Ixpe 0.1~0.5mm 0.5~3mm, 3~10mm
Color: black,white and gray,other colors can be customized
Shore hardness: 10~80 degree
Reflective:96%~97%
Structure:Closed cell
Surface smooth: Alu
Flammability:B1 grade
Refractoriness:100-150 degree
Thermal Conductivity:0.040~0.095 w/m.k
Water Absorption:(23degree,24h) 0.2~0.6%
Tearing Strength: 0.2~1.8 KN/m
Elongation at break :100%~240%
Tensile Strength: 0.2~1.6 Mpa
Compressed distortion: 2%~10%
Size change rate: -4%`-8%
Thermal conductivity: 0.040 ~0.095 w/m.k
Company info
CYG TEFA is the earliest PE foam manufacturing with scale
production in China since 2002.Mainly produce XPE FOAM,IXPE
FOAM,IXPP FOAM and ESD PRODUCT(Foam type: PE/EVA/PU/EPE/PP
Plastic).Annual production capacity is about 6000 tons.2 bases one
in Shen zhen and an other in Huzhou,with total 17 production
lines.CYG Management control system: Kingdee / OA / Oracle.CYG have
a professional team and technology.More than 30 R&D
staff.Through the great variety of our products we provide people
with a warm and quiet home and working environment.
- Management control system: Kingdee / OA / Oracle
11 employee
Investment rate: 4% to 10%
Responsible for : Improving available product / Technology
improving / New product development / New devices
IXPP project (three years: Proposal stage - Develop - Sampling -
Approved product- Small quantity supply for testing